High transparent laminated glass interlayer EVA film - FD-025/038/050/076

1. EVA film, 2.Laminated glass interlayer EVA film, 3. Strong adhesive, 4. High tensile strength, 5.Transparent, translucent - details see: https://www.packinghere.com/high-transparent-laminated-glass-interlayer-eva-film-10037451

Material: EVA	Type: plastic film	Usage: adhesive material	Feature: Moisture Proof
Hardness: Soft	Processing Type: Casting	Transparency: Transparent	Place of Origin: Shandong China (Mainland)
Brand Name: Fangding	Model Number: FD-025/038/050/076	Film: Clear and colored	Film type: Transparent, translucent, opaque
EVA transparency: More than 85%	Shrinkage ratio: ≤3.0 %	Long elongation(%): >180	Max width: 2300mm
Thickness: 0.25-0.76mm EVA interlayer film	Weatherability: heat and humidity resistance, anti-aging	Package: 3 rolls/case	Shipping: By Sea or carrier(DHL, FedEx, UPS..)

High transparent laminated glass interlayer EVA film

Introduction

1) Using EVA Film makes possible adhesion at low temperature, facilitating system operation, it can produce the products which is same by using autoclaves

2) It can produce the laminated glass,which could be used for building, fitment, industrial uses, etc. and also can produce various function glass, such as artistic laminated glass, etc,can be by produced by means of FANGDING Vacuum heating laminating machine

3) Glass can be laminated with a patterned cloth,papar,printed polyester,so the glass with a wide variety of decorative uses can manufactured

Characteristics

1) None absorb moisture, water absorption is lower than 1%, can be preserved in normal temperature and humidity.

2) The cost is lower than PVB ,can apply with low temperature and low pressure, lower prounction cost and less investment.

3) Not including plasticizer, high agglutinate performance to plastic, metal sheet, paper, etc.

4) Short production cycle.

5) Complied with national standard of GB9962-99.

EVA film main technical parameters

Test item	Architectural project-VE	Architectural project-EN
Tensile strength	8.1MPA	6.41MPA
Adhesion of glass	99.7N/cm(180° pealing)	94.6N/cm(pealing)
Adhesion of organic polymer film	21.3N/cm(180° pealing)	15.4N/cm(180° pealing)
High transmittance	85%	85%
Haze	0.47%	0.50%
UV blocked rate	98%	98%
Elongation	800%	880%
Shrinkage	≤3%	≤3%
Water absorption	≤0.01%	≤0.01%
Heat-resistance in the 100°c water for 2hrs 100°c	No bubbles, no delamination	No bubbles, no delamination
Humidity-resistance(60°c,95%RH:400hrs)	No bubbles or haze appeared	No bubbles or haze appeared
Anti-aging(50°c,65%RH,radiation 3000hrs)	Light change≤3.0%, no yellow change	Light change≤3.0%,no yellow change
Heat and cold shock(cold -40°c 30min,50circles)	No delamination and bubbles	No delamination and bubbles
Impact resistance against shot-bag	Qualified	Qualified
Ball impact peeling resistance	Qualified	Qualified
useful life	≥15 years	≥15 years